Optimal level of Au nanoparticles on Pd nanostructures providing remarkable electro-catalysis in direct ethanol fuel cell

5 years ago

Optimal level of Au nanoparticles on Pd nanostructures providing remarkable electro-catalysis in direct ethanol fuel cell

The designing and fabrication of economically viable electro-catalysts for ethanol oxidation reaction (EOR) in direct ethanol fuel cell (DEFC) has been one of the challenging issues over the decades. The present work deals with controlled synthesis of Pd coupled Au nano structure, as the non Pt group of catalysts for DEFC. The catalytic proficiency of bimetallic NPs (2–10 nm) are found to be strongly dependent on the Pd:Au ratio. The over voltage of EOR is considerably reduced by ∼260 mV with 33% of Au content in PdAu composition compared to Pd alone, demonstrating the beneficial role of Au and/or its surface oxides providing oxygen species at much lower potentials compared to Pd. The catalysts are further subjected to electrochemical analysis through voltammetry along with the temperature study on activation parameters. The quantitative determination of EOR products during the electrolysis is carried out by ion chromatographic analysis; vis-a-vis the coulombic efficiency of the product yield were derived from each of the compositions. Furthermore, a strong correlation among catalytic performances and bimetallic composition is established by screening the catalysts in an in-house fabricated direct ethanol anion exchange membrane fuel cell, DE(AEM)FC. The performance testing demonstrates outstanding increase of peak power density (∼40 mWcm⁻², 93%) for the best accomplishment Au (33%) covered Pd (67%) catalyst in comparison with the monometallic Pd.

Publisher URL: www.sciencedirect.com/science

DOI: S0378775317308467