Diamond Phase (sp3-C) Rich Boron-Doped Carbon Nanowalls (sp2-C): Physicochemical and Electrochemical Properties

Diamond Phase (sp3-C) Rich Boron-Doped Carbon Nanowalls (sp2-C): Physicochemical and Electrochemical Properties
J. Ryl, B. Dec, S. Gupta, S. B. Carrizosa, R. Bogdanowicz, K. Siuzdak, K. Darowicki, M. Ficek, M. Sawczak, M. Sobaszek
The growth of B-CNW with different boron doping levels controlled by the [B]/[C] ratio in plasma, and the influence of boron on the obtained material’s structure, surface morphology, electrical properties, and electrochemical parameters, such as −ΔE and k°, were investigated. The fabricated boron-doped carbon nanowalls exhibit activity toward ferricyanide redox couple, reaching the peak separation value of only 85 mV. The flatband potential and the concentration of boron carriers were estimated in the B-CNW samples using the Mott–Schottky relationship. It was shown that the vertically oriented carbon planes are characterized by p-type conductivity and very high hole-acceptor concentration (3.33 × 1023 cm–3 for a highly doped sample), which provides high electrical conductivity. The enhanced electrochemical performance of B-CNWs electrodes is an advantageous feature that can be applied in ultrasensitive detection or energy storage devices.

Publisher URL: http://dx.doi.org/10.1021/acs.jpcc.7b06365

DOI: 10.1021/acs.jpcc.7b06365

You might also like
Never Miss Important Research

Researcher is an app designed by academics, for academics. Create a personalised feed in two minutes.
Choose from over 15,000 academics journals covering ten research areas then let Researcher deliver you papers tailored to your interests each day.

  • Download from Google Play
  • Download from App Store
  • Download from AppInChina

Researcher displays publicly available abstracts and doesn’t host any full article content. If the content is open access, we will direct clicks from the abstracts to the publisher website and display the PDF copy on our platform. Clicks to view the full text will be directed to the publisher website, where only users with subscriptions or access through their institution are able to view the full article.